Titanium Anode

Message

Product Name: Titanium Anode

Base material: Gr1, Gr2

Coating: Ruthenium-Iridium oxide coating, Ruthenium-Titanium coating; 

PT/IR/Ru Coated Titanium Anode/Mmo Coating Titanium Sheets Anode/Electrode Dsa

Size: Thickness ≥ 1.5mm, width ≤ 1200mm, length ≤ 6000mm 

Tray Size: 20*960*960mmTitanium Mesh Size: 1.5*887*887mm

Baffles: Gr2 Ti Plate Thickness 2.0mm  Custom-made size available

Shapes: Sheet, Plate, Round, Tube, Mesh, Titanium Basket for Electroplating/ Ti Basket;

Customized Shapes

Status: Annealed

Application: Papermaking, Food, Construction, Ocean, Aerospace, Aviation, Electronics, 

Metallurgy, Pharmacy, Salt, Chemical, Petroleum

Active coating titanium anodes (DSA)

Products Recommended

Firmakes Titanium could make different sizes and shapes according to designed drawing by clients, so as to obtain the best effects.

Titanium anode coating, which consists of mixed metal oxide (MMO), such as RuO2 (Ruthenium)--the RuO2 coating thickness ≥ 10um, IrO2 (Iridium)--the IrO2 coating thickness ≥10um, TiO2,Ta2O5 (Tantalum), Pt (Platinium)--0.5-5 micron, PbO2--the PbO2 coating thickness 0.6-1mm, can distinctly reduce cell voltage during the electrolysis of chlorine evolution, oxygen evolution and have remarkable energy-saving effect and longer lifetime. The substrate is GR1 or GR2 titanium material, which can be reused and re-costed. Titanium anode is also called as DSA or insoluble titanium anode due to its dimension stability and high corrosion resistivity. With such advantages, titanium anode won't pollute electrolysis system and increase final products purity, reduce the maintenance cost of the equipment. 

DSA titanium anode application fields:

Copper recovery in etching liquid, electrodialysis industry, MMO cathodic protection, sewage treatment, swimming pool disinfection, electrolysis, sodium hypochlorite generator, chlor-alkali industry, water heater anticorrosion, lonized water electrolysis, electroplating, hydrometallurgy. 

DSA titanium anode available shapes: sheet, wire, mesh,tube, ring, strip, mesh basket, etc.

Titanium Anode used for Chlor-Alkali Industry

27[T_M}Titanium Anode.jpg

1. Substrate Metal Chemical Composition:

Grade

N

C

H

Fe

O

Ti

Gr1

0.03

0.08

0.015

0.20

0.18

bal

Gr2

0.03

0.08

0.015

0.30

0.25

bal

Substrate Metal Mechanical Properties:

Grade

Tensile   strength(min)

Yield   strength(min)

Elongation   (%)

ksi

MPa

ksi

MPa

Gr1

35

240

25

170

30

Gr2

50

345

40

275

25

2. MMO Coating: Mixed Ruthenium-Iridium Oxide

Coating

Oxygen   revolution potential

Suitable   working environment

Mixed   Ruthenium and Iridium

<1.13V

Solution   contains Cl-, PH>=7

Coating Contents and Life Span:

8grams/m2

10grams/m2

12grams/m2

15grams/m2

20grams/m2

6,000   hours

8,000   hours

10,000   hours

12,000   hours

13,500   hours

3. Working Parameters for Ru-Ir Coating:

Current   density

Temperature

Chlorine   concentration

Polarity   reversal

Reversal   frequency

<500A/m2

40-60°C

About   30grams/liter

suitable

2-4   hours


Important note: If above product specifications don’t meet your requirements, please kindly let me know. We could customize the products as per your requirements.